Specifications

CAS NO: 9002-88-4
HS Code: 39012000
Apperance: granule&pellets

High Quality LLDPE Recycled Granules

1, LLDPE film grade

Tests	Value	Unit
Melt Flow Rate (MFR)	2.0±0.4	g/10min
Density	920±2	Kg/cm3
Tensile Strengthat Yield	8	Mpa ≥
Tensile Strengthat Break	12	Mpa ≥
haze	15	%≤
Packing	In 25 kg PP woven bags,20MT/20’FCL

 

2, LLDPE for Master Batch Use 

  

Tests	Value	Unit
Melt Flow Rate (MFR)	20	g/10min
Density	0.924	g/cm3
Tensile Strength	MD12	Mpa
	TD 10
Elongation at Yield	13	%
Elongation at Break	200
Dark Drop Impact	105	g
Brittle Temperature(F 50)	-70	°C
Vicat Softening Point	90	°C
Packing	In 25 kg PP woven bags,20MT/20’FCL

 

3, LLDPE Powder Rotational Molding Grade for Tank Use

Tests	Value	Unit
Melt Flow Rate (MFR)	3.2	g/10min
Density	0.939	g/cm3
Melting Point	127	°C
Tensile Yield Strength	21	Mpa
Tensile Strength at Break	28	Mpa
Elongation at Break	1,100	%
Flexural Modulus	750	Mpa
Brittle Temperature	<-60	°C

Application

1 Fiber (Carpet, Textiles, Upholstery, etc.)

2 Film (Shopping bags, casting film, multilayer film, etc.)

3 Blow Molding (Medical & Cosmetic container, Lubricant & Paint container, etc)

4 Extrusion Molding (Sheet, Pipe, Wire & Cable, etc.)

5 Injection Molding (Automotive, Electronic, Construction, House wares, Furniture, Toys, etc.)

---